Contributing Writer
- FMA
- The Fabricator
- FABTECH
- Canadian Metalworking
Categories
- Additive Manufacturing
- Aluminum Welding
- Arc Welding
- Assembly and Joining
- Automation and Robotics
- Bending and Forming
- Consumables
- Cutting and Weld Prep
- Electric Vehicles
- En Español
- Finishing
- Hydroforming
- Laser Cutting
- Laser Welding
- Machining
- Manufacturing Software
- Materials Handling
- Metals/Materials
- Oxyfuel Cutting
- Plasma Cutting
- Power Tools
- Punching and Other Holemaking
- Roll Forming
- Safety
- Sawing
- Shearing
- Shop Management
- Testing and Measuring
- Tube and Pipe Fabrication
- Tube and Pipe Production
- Waterjet Cutting
Industry Directory
Webcasts
Podcasts
FAB 40
Advertise
Subscribe
Account Login
Search
Welding ASTM A514 or A514M-05 steel?
Before you do, take a close look at filler metals, heat input
- By Dean C. Phillips
- June 12, 2007
- Article
- Arc Welding
Cost and efficiency dictate manufacturing and fabricating trends in most industries. In addition to implementing lean work flow practices—better, faster transportation and processing and minimal inventory—many companies turn to the use of higher-strength, lighter-weight materials to reduce costs and improve welding productivity.
ASTM A514 and A514M-05 high-strength, low-alloy, quenched-and-tempered steels are among these materials. Although they have been available for many years, they continue to pose some distinct challenges for welders. Welding these materials successfully is a matter of understanding some key factors, including filler metal choices and preheating and interpass heat requirements.
What It Is, Why It Is
ASTM A514 is a specification for 100 kilopounds-per-square-inch-yield, low-alloy, quenched-and-tempered steel intended for structural applications and is typically known in the industry as USS (United States Steel) nomenclature T1®, regardless of the manufacturer.
A514 grades are A, B, E, F, H, P, Q, and S. Each grade has a unique chemistry and may differ in the maximum thickness to which it is rolled, from 1¼ in. to 6 in. The material thickness affects the mechanical properties. For instance, A514 rolled to 2½ in. or less must have 110-KSI to 130-KSI tensile strength, 100-KSI minimum yield strength, and 18 percent elongation. For materials 2½ to 6 in. thick, the mechanical properties are 100-KSI to 130-KSI tensile strength, 90-KSI minimum yield strength, and 16 percent elongation.
The hardness for material thickness up to and including ¾ in. is 235 to 293 HBW (Brinell). Note that the specification does not list hardness requirements for materials thicker than ¾ in.
One of the reasons for the difference in properties among these thicknesses is the quenching. The thicker the material, the slower the quench rate, which results in lower minimum yield and tensile strengths.
Typically, this material is used for structural applications. In many cases, the term structural refers to buildings, but the material also is used in heavy equipment structures to reduce weight and improve payload capacity, such as in railcars and their components, large mining truck frames, semitrailer frames, and crane boom sections.
Because the typical hardness of the materials is 22 to 27 Rockwell C, it is also used for wear strips, cutting edges, and side cutters. Typical applications are backhoe buckets and other wear components in earthmoving equipment.
Making the Choice: Filler Metals
Welding A514 is not complicated when some precautions, especially with filler metal choices, are used.
A primary concern is filler metal hydrogen content. You should not use filler metals that deposit weld metal with diffusible hydrogen content greater than 8 ml per 100 grams of deposited weld metal. A514 is sensitive to diffusible hydrogen, which may result in hydrogen cracking.
Filler Metal Selection ASTM A514 and A514M-05 Up to 2½ In. Thick |
||
---|---|---|
Welding Process | AWS A5 Specification | Classification |
SMAW | A5.5/A5.5M-2005 | E11018M or E12018M |
GMAW | A5.28/A5.28M-2005 | Solid electrodes ER 110S-1 and ER120S-1 or Metal-cored electrodes E110C-K3, E110C-K4, and E120C-K4 |
FCAW | A5.29/A5.29M-2005 | E11XT1-K3C and -K3M E11XT5-K3C and -K3M E11XT5-K4C and -K4M E12XT5-K4C and -K4M |
SAW | A5.23/A5.23M-1997 | Solid electrode/flux combination F11AX-EXXX-XXX and F12AX-EXXX-XXX or Composite electrode/flux combination F11AX-ECXXX-XXX and F12AX-ECXXX-XXX |
The filler metal strength depends on the application of the A514. Figure 1 shows filler metals you can use to match the strength of base materials up to 2½ in. thick where the same mechanical properties as the base material are required. On base material thicknesses greater than 2½ in., you can use the same filler metals, but their strength exceeds that of the base metal, a condition called overmatching strength (see Figure 2).
Filler Metal Selection ASTM A514 and A514M-05 Greater Than 2½ Inches Thick |
||
---|---|---|
Welding Process | AWS A5 Specification | Classification |
SMAW | A5.5/A5.5M-2005 | E10018M |
GMAW | A5.28/A5.28M-2005 | Solid electrodes ER 100S-1 or Metal-cored electrodes E100C-K3 |
FCAW | A5.29/A5.29M-2005 | FCAW A5.29/A5.29M-2005 E10XT1-K3C and -K3M E10XT5-K3C and -K3M E10XT1-K7C and -K7M E10XT1-K9C and -K9M |
SAW | A5.23/A5.23M-1997 | Solid electrode/flux combination F10AX-EXXX-XXX or Composite electrode/flux combination F10AX-ECXXX-XXX |
When joining A514 to other low-alloy steels or carbon steels of lower strength, use a filler metal with strength that meets the lower-strength base material's properties. For example, when welding ASTM A36 to A514, use a 70-KSI-tensile-strength electrode to match the lower-strength material. Don't focus solely on strength; keep the hydrogen cracking risk in mind.
Heat Input Control
Even though A514 is readily weldable, excessive preheat and interpass temperatures and welding heat input can affect the alloy's chemical properties. Figure 3 lists typical preheat and interpass temperatures for A514. These temperatures apply whether you are welding A514 to itself or to other, lower-strength materials.
Preheat and Interpass Temperatures | ||
---|---|---|
Thickness (In.) | Minimum Preheat and Interpass Temperature (F) |
Maximum Preheat and Interpass Temperature (F) |
Up to ¾ | 50 | 400 |
¾ to 1½ | 125 | |
1½ to 2½ | 175 | 400 |
More than 2½ | 225 |
It should be noted that preheat and interpass temperatures higher than those shown in Figure 3 may alter the mechanical properties of the material. Tempil® Sticks, contact pyrometers, infrared thermometers, or other heat-measuring devices should be used to control preheat and interpass temperatures.
In addition to the preheat and interpass temperature controls, heat input, which is a function of amperage, voltage, and travel speed, must be restricted. Heat input is expressed in joules per inch. The formula is:
- Heat Input (joules/in.) = (Amperage x Voltage x 60) ÷ Travel Speed (IPM)
Typical heat input is about 55,000 joules per in. (±20 percent). For other heat inputs, it is advisable to contact the steel manufacturer for recommendations.
As a final precaution, A514 is not intended to be used in the postweld heat-treated (PWHT) condition, as it will alter the mechanical properties for which the material was intended.
Other sources of information for welding A514/A514M-05 steel are the steel manufacturers' fabrication guides and:
- AWS D1.1, Structural Code—Steel
- D14.3, Specification for Welding
- Earthmoving, Construction, and
- Agricultural Equipment
- D15.1, Railroad Welding Specification—Cars and Locomotives.
Want more information?
Visit www.thefabricator.com; enter the article number (digits only) in the home page search box:
- "Cracking the case" 1397
- "MIG—welding tips and resources" 1083
- "Preventing welding-related fires" 952
About the Author
Dean C. Phillips
101 Trade Square
Troy, OH 45373
937-332-4000
Related Companies
subscribe now
The Fabricator is North America's leading magazine for the metal forming and fabricating industry. The magazine delivers the news, technical articles, and case histories that enable fabricators to do their jobs more efficiently. The Fabricator has served the industry since 1970.
start your free subscription- Stay connected from anywhere
Easily access valuable industry resources now with full access to the digital edition of The Fabricator.
Easily access valuable industry resources now with full access to the digital edition of The Welder.
Easily access valuable industry resources now with full access to the digital edition of The Tube and Pipe Journal.
Easily access valuable industry resources now with full access to the digital edition of The Fabricator en Español.
- Podcasting
- Podcast:
- The Fabricator Podcast
- Published:
- 05/07/2024
- Running Time:
- 67:38
Patrick Brunken, VP of Addison Machine Engineering, joins The Fabricator Podcast to talk about the tube and pipe...
- Trending Articles
White House considers China tariff increases on materials
A deep dive into a bleeding-edge automation strategy in metal fabrication
Majestic Steel Arkansas fully operational
A visit to Automate 2024 reveals the future might be now
Rivian to expand Illinois facility to manufacture midsized SUV
- Industry Events
Laser Welding Certificate Course
- May 7 - August 6, 2024
- Farmington Hills, IL
World-Class Roll Forming Workshop
- June 5 - 6, 2024
- Louisville, KY
Advanced Laser Application Workshop
- June 25 - 27, 2024
- Novi, MI
Precision Press Brake Certificate Course
- July 31 - August 1, 2024
- Elgin,